ARISTOCRATE NICKEL BRIGHTNER – 009 V/B

ARISTOCRATE NICKEL BRIGHTNER – 009 V/B

Product Details:

X

Product Description

ARISTOCRATE NICKEL BRIGHTNER - 009 V/B


BETTER PERFORMANCE BRIGHT NICKEL PROCESS. 

Aristocrate Nickel Process is a better performance process  developed to produce  superior Leveled, Ductile, Brilliant  deposits or mirror finish with uniform brightness at  medium and low current density area, acceptable coverage and better Chrome receptivity.

 

The Process employs two addition agents namely Aristocrate Nickel Brightner 009V/B and additive 022/502/622. Both the addition agents are required for initial bath make up and for replenishing primary and secondary brightner components during working of the bath solution. The process gives excellent performance over a wide range of operating bath concentration, Temperature, Current densities etc. And can be used for either rack or barrel plating application with air or mechanical agitation.

 

The process is used for decorative plating either for a single layer Bright Nickel or as the top layer over Semibright Nickel for improved corrosion resistance. This process can be used on different base metals such as M.S. Copper, Semibright Nickel and on Brass, Zinc and Zinc Alloys components with a previous copper plating from a Cyanide based process while on Aluminum and Aluminum Alloys after suitable pretreatment followed by Zincating and Cyanide Copper plating.

 SALIENT FEATURES :

1.       Faster rate of brightening provides desired finish with less thickness of  the deposits.

2.       Produce extremely good leveling resulting in shorter plating time and fewer polishing operations.

3.       Excellent low current density brightness and coverage.

4.       Excellent deposit ductility and Chrome receptivity.

5.       Good tolerance to metallic impurities.

 

BATH MAKE-UP :

                                                                                                                RANGE                    OPTIMUM

Aristocrate Bright Nickel Salt – 531 R                             gm/lit.                     200-400                       325

Aristocrate Bright Nickel Additive-022/502/622                 gm/lit      (Vat)       6.0-10.0                          8.0

                                                                                                           (Barrel)  4.0 “ 8.0                         6.0

Aristocrate Nickel brightner “ 009                                                      (  Vat)       0.4- 0.6                        0.6

Aristocrate Nickel brightner-009                                                           (Barrel)   0.2-0.6                           0.4

 

WORKING CONDITIONS :

                                                                                                                                RANGE                 OPTIMUM

Density o Be                                                                                                          16-26                           22

Temperature o C                                                                                                     40-60                           50

PH (Electrometric)                                                                                  (Vat)       4.4-5.2                         4.8

                                                                                                                 (Barrel)  4.0-4.8                          4.4

Cathode Current Density                                             (Vat)Amp/Sq.dm                 2.0-8.0                          4.0

                                                                                    (Barrel)Amp./Sq.dm           0.5-2.0                          1.0

 

Anode Current Density                                                 (Vat) Amp/Sq.dm.               1.0-4.0                           2.0

                                                                                       (Barrel)Amp./Sq.dm           0.5-2.0                           1.0

Voltage                                                                     (Vat)                                       4.0-12.0                         5.5

                                                                                     (Barrel)Amp./Sq.dm.          8.0-16.0                        12.0

 

Agitation                                                                                          Cathode Rod/Low                              Air

 

                                                                                                      Pressur Air

Foltration                                                                                      continuous                                            continuous

 

Rate of Deposition at

3 Amp./Sq.dm.per minute                                                       0.50 Micron                                          0.58 Micron

 

 

BATH MAINTENANCE :

 

                                                                                                           RANGE                           OPTIMUM

 

Nickel Metal                                         gm/ltr.                                    43-70                                     61.0

Nickel Sulphate                                    gm/ltr.                                    170-270                                 230.0

Nickel Chloride                                    gm/ltr.                                    35-55                                     48.0

Boric Acid                                             gm/ltr.                                    30-50                                     45.0

TABLE :-

NO.

PLATING QUANTITY

ADDED IN ML PER 1000 AMP/HR.

 

 

Brightner 009 V/B

Additive 022/502/622

Leveller 544/644

1.

Barrel Plating

100-200

50-100

200-300

150-250

--

NOT REQUIRED

2.

Low Thickness

(4-10 Microns)

100-150

75-100

300-250

200-250

--

NOT REQUIRED

3.

Medium Thickness

(12-15 Microns)

75-125

100-125

275-225

200-250

Preferable

50-75

4.

Higher Thickness

(Above 20 Microns)

50-100

80-100

200-250

225-250

Preferable

35-50

  



Contact Details

GST : 24AABCM0632N1ZM
"Mahavir Estate", Behind Shah Chambers, Near CTM Cross Lane, Amraiwadi, Ahmedabad - 380026, Gujarat, India
Phone :View Number
Send Inquiry
Key Personnel
Mr. VINOD L SHAH (Managing Director)
Mobile :View Number